A Study on Preparation and Property of Calcium Alginate Drug -Loaded Microspheres by High Voltage Electrostatic Field Technology

WANG Zongxin,ZHANG Yongjun,CHEN Weiming,XU Yong,ZHOU Guangdong   

  • Received:2019-04-03 Revised:2019-05-12 Online:2019-06-20 Published:2019-06-20
  • Contact: 国家重点研发计划(2017YFC1103900)

摘要： 目的 探索高压静电场技术制备藻酸钙微球的最佳参数组合,以期微球直径更小更均匀,并研究其载药后的缓释行为。方法 设置不同的电压、CaCl2浓度、藻酸钠浓度、离心机转速、针头直径,观察微球直径和表面形态,以直径更小更均匀为标准,筛选最佳参数组合。负载低（L组）、中（M组）、高（H组）3种浓度的牛血清白蛋白,对比3组的包封率和载药率,并绘制累计缓释曲线,观察其体外缓释行为。结果 16 KV电压、1M CaCl2浓度、0.5%藻酸钠浓度、200 r/min和30 G的针头是最佳参数组合。L、M、H各组的包封率分别为（91±1.46）%、（85±1.63）%和（79±3.29）%,载药率分别为（0.89±0.04）%、（2.56±0.57）%和（4.10±1.21）%。3组药物都可以持续释放超过28 d,缓释时间较长,释放行为稳定、规律。结论 利用最佳参数组合制备的藻酸钙微球是一种优良的药物缓释载体。

关键词: 高压电场, 藻酸钠, 微球, 缓释

Abstract: Objective To explore the optimal combination parameters of calcium alginate microspheres by using high voltage electrostatic field technology,and to make microspheres with smaller and more uniform diameters for further study of the sustained release behavior of microspheres after drug loading.Methods Different voltage,CaCl2 concentration,and sodium alginate concentration were set.The centrifuge speed and needle diameter were observed.The diameter and surface morphology of the microspheres were observed.The optimal combination parameters were selected with smaller and more uniform diameters.Low,medium and high loads,three concentrations of bovine serum albumin,were named group L,group M and group H respectively.The encapsulation efficiency and drug loading rate of the three groups were compared.The cumulative slow-release curve was drawn and the sustained-release behavior in vitro was observed.Results Voltage of 16 KV,1 M CaCl2 concentration,0.5%sodium alginate concentration,200 r/min and 30 G needle were the best combination parameters.The encapsulation rates of group L,M and H were(91±1.46)%,(85±1.63)%,(79±3.29)%respectively.And the drug loading rates were(0.89±0.04)%,(2.56±0.57)%,(4.10±1.21)%respectively.All the three groups of drugs could be sustained for more than 28 days,the sustained release time was longer,and the release behavior was stable and regular.Conclusion The calcium alginate microspheres produced by using the optimal combination parameters are excellent drug delivery vehicles.

Key words: High voltage electric field, Sodium alginate, Micr